特性/ Features
耐CAF性能
Anti-CAF capability
无卤素 Tg≧150℃
Halogen-Free,Tg≧150℃
优良的通孔可靠性
Excellent T/H reliability
优异耐热性 Td ≥325℃ ,T288≥5min
Excellent thermal resistance ,Td ≥325℃ ,T288≥5min
低Z轴膨胀系数
Low Z-CTE≤ 3.5%
应用领域/ Applications
手机、电脑、通讯设备、汽车电子、摄像机、电视机等。
Mobile phone, Computer,Communication equipment , Automotive electronics, VCR,Television, etc.
主要特性 / General properties
检测项目 Item | 单位 Unit | 检测条件 Test Condition | 测试方法IPC-TM-650 | 典型值 Typical Value | ||
玻璃化转变温度Tg | ℃ | DSC | 2.4.25 | 156 | ||
剥离强度1oz Peel Strength | N/mm | 288℃, 10S | 2.4.8 | 1.42 | ||
热应力 Thermal stress | S | 288℃,solder dip | 2.4.13.1 | 180 s No delamination | ||
弯曲强度 Flexural Strength | N/mm2 | LW/CW | 2.4.4 | 536/433 | ||
燃烧性 Flammability | Rating | E 24/125 | UL94 | V-0 | ||
表面电阻 Surface Resistivity | MΩ | After moisture | 2.5.17.1 | 5.21×107 | ||
体积电阻 Volume Resistivity | MΩ·cm | After moisture | 2.5.17.1 | 5.10×108 | ||
介电常数 Dielectric Constant | - | C 24/23/50 | 2.5.5.9 | 4.6 | ||
介质损耗角正切 Loss Tangent | - | C 24/23/50 | 2.5.5.9 | 0.014 | ||
耐电弧 Arc Resistance | S | D48/50+D0.5/23 | 2.5.1 | 120 | ||
击穿电压 Dielectric Breakdown | KV | D48/50+D0.5/23 | 2.5.6 | 57 | ||
吸水率 Moisture Absorption | % | D24/23 | 2.6.2.1 | 0.12 | ||
热分解温度Td | ℃ | Weight Loss 5% | 2.2.24.6 | 372 | ||
T288(不覆铜) | min | TMA | 2.4.24.1 | 60 | ||
CTE Z-axis | Alpha 1 | ppm / ℃ | TMA | 2.4.24 | 45 | |
Alpha 2 | ppm / ℃ | 2.4.24 | 245 | |||
50 - 260 ℃ | % | 2.4.24 | 2.5 | |||
卤素含量 Halogen content | Cl | ppm |
A |
EDX-GP | ≤900 | |
Br | ≤900 | |||||
Cl+Br | ≤1500 |
Specimen Thickness : 1.6mm ; Specification sheet:IPC-4101D/128,is for your reference only
半固化片介绍-H160HFPP/ Prepreg instruction
H160HFP P (UV Prepreg):
prepreg type | Resin Content(%) | 压合厚度Cured thickness(mm/mil) | ||||
R/C(%)含量 | 公差Tolerance | Nominal | Range(±)mil | |||
% | ± | mm | mil | mm | mil | |
7628HRC | 52 | 2 | 0.227 | 8.93 | 0.023 | 0.9 |
50 | 2 | 0.217 | 8.54 | 0.022 | 0.8 | |
48 | 2 | 0.206 | 8.11 | 0.020 | 0.8 | |
7628 | 45 | 2 | 0.192 | 7.56 | 0.019 | 0.8 |
43 | 2 | 0.183 | 7.20 | 0.018 | 0.7 | |
1506 | 52 | 2 | 0.175 | 6.89 | 0.018 | 0.7 |
50 | 2 | 0.168 | 6.61 | 0.017 | 0.7 | |
48 | 2 | 0.162 | 6.38 | 0.017 | 0.6 | |
2116 | 59 | 2 | 0.135 | 5.31 | 0.013 | 0.5 |
57 | 2 | 0.130 | 5.12 | 0.013 | 0.5 | |
55 | 2 | 0.123 | 4.84 | 0.013 | 0.5 | |
53 | 2 | 0.117 | 4.61 | 0.011 | 0.5 | |
1080 | 70 | 2 | 0.089 | 3.50 | 0.009 | 0.4 |
68 | 2 | 0.084 | 3.31 | 0.008 | 0.3 | |
66 | 2 | 0.079 | 3.11 | 0.008 | 0.3 | |
64 | 2 | 0.074 | 2.91 | 0.007 | 0.3 | |
106 | 78 | 2 | 0.064 | 2.52 | 0.006 | 0.3 |
75 | 2 | 0.056 | 2.20 | 0.006 | 0.2 | |
73 | 2 | 0.051 | 2.01 | 0.005 | 0.2 |
建议压制程式: Suggest cycle
储存条件:温度≤23℃、湿度≤50%,保存时间3个月;温度≤5℃、密封条件下,保存时间6个月.
Storage Condition: T≤23℃& ≤50%RH,Within 3 months; T≤5 ℃ Within 6 months (seal condition).
在上述要求内,我司可立即安排PP送样;若有特殊要求,由供需双方商定。Follow above condition,
Our company will arrange sample immediately. We can discuss if you have special requirement.