FEATURES
High Tg: ≥200℃ (DMA)
Low Dk:≤3.7,10GHz
Low Df:≤0.0047, 10GHz
Excellent thermal resistance, Td≥340℃
Low Z axis CTE
Low water absorption, excellent anti-CAF, high reliability
Compatible with Lead-free
APPLICATIONS
Server
Switch
Base station
Optical module
Millimeter wave radar for Automotive
High performance computing
GENERAL PROPERTIES
Item | Test Condition | Unit | Spec | Typical value | ||
TG | TMA | ℃ | ≥185 | 190 | ||
DMA | ℃ | ≥200 | 215 | |||
Peel Strength 1oz Very low profile copper | RTF | As Received | N/mm | ≥0.53 | 0.70 | |
HVLP | As Received | N/mm N/m㎡ | ≥0.53 | 0.65 | ||
Thermal stress | 288℃, solder dip | S | >10 | >180s No delamination | ||
Flexural Strength | LW | N/m㎡ | ≥345 | 525 | ||
CW | ≥345 | 485 | ||||
Flammability | E 24/125 | - | UL94V-0 | V-0 | ||
Surface Resistivity | After moisture | MΩ | ≥1.0x105 | 1.56x108 | ||
Volume Resistivity | After moisture | MΩ·cm | ≥1.0x106 | 2.21x109 | ||
Dielectric Constant (Rc54%) | 10GHZ C 24/23/50 | - | ≤3.7 | 3.65 | ||
Loss Tangent(RC54%) | 10GHZ C 24/23/50 | - | ≤0.0047 | 0.0045 | ||
Arc Resistance | D 48/50+D 0.5/23 | S | ≥60 | 120 | ||
Dielectric Breakdown | D 48/50+D 0.5/23 | KV | ≥40 | 60 | ||
Moisture Absorption | D 24/23 | % | ≤0.2 | 0.08 | ||
Td | Weight Loss 5% | ℃ | ≥340 | 408 | ||
CTE in XY/Z Axis | Alpha1 | TMA
| ppm/℃ | ≤45 | 35 | |
Alpha2 | ppm/℃ | ≤280 | 203 | |||
50 - 260°C | % | ≤2.8 | 2.0 | |||
T288(Unclad) | TMA | min | ≥15 | >60 | ||
T300(Unclad) | TMA | min | ≥2 | >60 | ||
u Specimen thickness :0.762mm
u Specification sheet:IPC-4101E/102，is for your reference only.
u Explanation: C: Humidity conditioning D: Immersion conditioning in distilled water
E: Temperature conditioning